Tenders Are Invited For Supply Of Leather in Jordan

Work Detail

Tenders Are Invited For Supply Of Leather. A. Upper Leather: 1. Total Ash (%): 3-7 2. Tensile Strength (Minimum) For 20 Readings: 180 Kg/Cm² 3. Tear Strength (Puncture Method): 120 Newtons (Minimum) 4. Elongation At Break: 35-80% 5. Water Absorption (Static) After One Hour: 100% (Maximum) 6. Water Absorption (Dynamic) After One Hour: 30% (Maximum) 7. Leather Thickness: 1.8 Mm (Minimum) 8. Flexing Resistance (Durability): 50,000 Cycles Without Deformation 9. Surface Shrinkage (Hot Water Method): None 10. Expansion: 5% (Maximum) 11. Chromium Oxide Content: 3% (Minimum) 12. Fat Content: 4% (Minimum) 13. Ph Value: 3.2 (Minimum) B. Sole: 1. Made By Direct Injection Method 2. Adhesion Strength To The Upper (Strip): 4 Newtons/Mm (Minimum) For Both Sole And Heel 3. Adhesion Strength To The Upper (Entire Shoe): - Sole To Leather: 400 Newtons (Minimum) - Heel To Leather: 500 Newtons (Minimum) 4. Abrasion Resistance: 150 Mm³ (Maximum Volume Loss) 5. Flexibility: The Crack Length Should Not Exceed 4 Mm After 30,000 Cycles. 6. Outsole Thickness (Measured From The Inside, Excluding Any Grooves Or Voids): 4 Mm (Minimum) 7. Heel Thickness: 2.5-4.5 Cm 8. Durability (Humidity 100%, Temperature 70 Degrees Celsius For Seven Days): The Crack Length Shall Not Exceed 6 Mm After 150,000 Cycles. 9. The Sole Must Be Slip-Resistant. C. Shoe Eyelets: 1. Eyelet Diameter: Appropriate For The Laces. 2. Number Of Eyelets And/Or Hooks Per Pair: 8 (±2), Evenly Distributed Along The Shoe. D. Insoles: 1. Insole Thickness: 2 Mm Minimum. 2. Made Of A Comfortable, Sweat-Absorbent Polymer Material. Disclosure Of Required Quantities And Sizes # Sizes Quantities 300 39 1 300 41 2 300 42 3 500 43 4 300 44 5 300 45 6 Appendix "C" Attached To The Supply Directorate Memorandum No.: Sg/Tf/Supply/Clothing/16/2025/ Dated Rajab 1447 January 2026 General Specifications Required For Beige High-Top Boots 1. General Specifications: A. The Supplied Quantity Must Match The Reference Sample In Terms Of Shape, Color, And Type Of Leather. B. The Upper Part Of The Boot Must Be Made Of Genuine Leather (Cow Split Leather) And Free From Visible Defects Such As Shrinkage, Stains, Cracks, Etc. It May Contain Fabric, Provided That This Fabric Is Nylon. C. The Manufacturing And Finishing Of The Boot Must Be Of High Quality. D. It Must Be Easy To Fasten And Unfasten. E. The Tongue Must Be Made Of Genuine Leather With A Thickness Of At Least 1 Mm, Or Made Of Synthetic Fabric Or Its Equivalent, And May Consist Of Layers Of Leather, Synthetic Fabric, And Sponge. F. The Threads Used For Stitching Must Match The Color Of The Shoe. G. The Laces Must Match The Color Of The Leather, Be 150-170 Cm Long, And Have A Tensile Strength Of At Least 500 Newtons. H. The Outsole Must Be Made Of Natural Rubber. I. The Outsole Must Not Contain Any Wires Or Nails In Any Part Of It, Including The Heel And The Inside, And Must Not Have Any Internal Voids. J. The Top Of The Shoe Collar Must Be Comfortable And Securely Attached To The Inside, And May Be Reinforced With A Layer Of Sponge And Fabric. K. The Shoe Must Be Lined On The Inside To Ensure Comfort And Absorb Sweat And Moisture. L. The Shoe Must Be Reinforced At The Front And Back With A Plastic Material Of Suitable Thickness, Not Less Than 1.6 Mm. M. The Height Of The Shoe Must Be 25 ± 2 Cm, Measured From The Back, Including The Heel Height 2. Interested Companies Are Invited To Obtain The Tender Documents From [Location/Department] Starting From [Date] Until [Date]. The Tender Documents Will Be Available For A Fee Of [Amount] Jordanian Dinars. 3. The Deadline For Submitting Bids Is [Date]. 4. Bids Will Be Opened At [Time] On [Date] At [Location]. 5. For Further Information, Please Visit The Royal Jordanian Air Force Website: (Www.Rjaf.Mil.Jo) Tender Link : Https://Www.Rjaf.Mil.Jo/Ar/Tenders.Html

Contact Information